Penerangan:
钐钴(SMCO)磁铁Dibuat Terutamanya Daripada Jarang Samarium Logam Bumi Dan Logam Kobalt Strategik,Dangan Besi,Tembaga,Zirkonium Dan Praseodiumium。
IA Mempunyai Prestasi Yang Tinggi Dan Pekali Suhu Rendah,Suhu Kerja Maksimum Adalah Seinghga 350℃。ia tidak perlu disalut kerana ia adalah sukar untuk蒙太斯丹特洛斯岛丹特洛斯岛大地马达,传感器,仪表,elektronik,jam唐南,kereta,普通蕉,Aeroangkasa dan aplikasi lain。
Terdapat Dua Siri Aloi磁铁SMCO:SMCO5 DAN SM2CO17。
Proves Pengeluaran Carta Alir:
磁性特性:
磨损 | aloi siri. | 布鲁斯 | HCB. | HCJ. | (BH)最大 | ||||
公吨 | GS. | Ka / M. | OE. | Ka / M. | OE. | KJ / M3. | 莫戈 | ||
XG16. | SMCO5. | 770-860. | 7700-8600. | 613-716. | 7700-9000 | ≥1194. | ≥15000 | 120-143 | 15-18 |
xg16h. | 770-860. | 7700-8600. | 613-716. | 7700-9000 | ≥1592 | ≥20000. | 120-143 | 15-18 | |
XG18 | 810-920. | 8100-9200. | 637-756. | 8000-9500. | ≥1194. | ≥15000 | 135-159 | 17-20 | |
XG18H. | 810-920. | 8100-9200. | 637-756. | 8000-9500. | ≥1592 | ≥20000. | 135-159 | 17-20 | |
XG20. | 850-950. | 8500-9500. | 637-756. | 8000-9500. | ≥1194. | ≥15000 | 151-175 | 19-22 | |
XG20H. | 850-950. | 8500-9500. | 637-756. | 8000-9500. | ≥1592 | ≥20000. | 151-175 | 19-22 | |
XG22. | 890-1000. | 8.900-10.000 | 661-772. | 8300-9700. | ≥1194. | ≥15000 | 167-191 | 21-24 | |
XG22H. | 890-1000. | 8.900-10.000 | 661-772. | 8300-9700. | ≥1592 | ≥20000. | 167-191 | 21-24 | |
XGS24M. | SM2CO17. | 920-1040 | 9.200-10.400. | 318-788. | 4000-9900. | ≥398 | ≥5000. | 175-199 | 22-25 |
XGS24. | 920-1040 | 9.200-10.400. | 661-796. | 8.300-10.000 | ≥1194. | ≥15000 | 175-199 | 22-25 | |
XGS24H. | 920-1040 | 9.200-10.400. | 661-804 | 8.300-10.100. | ≥1990. | ≥25000. | 175-199 | 22-25 | |
XGS26M. | 1000-1060 | 10.000-10.600. | 318-796. | 4.000-10.000 | ≥398 | ≥5000. | 191-215 | 24-27 | |
XGS26. | 1000-1060 | 10.000-10.600. | 677-820 | 8.500-10.300 | ≥1194. | ≥15000 | 191-215 | 24-27 | |
XGS26H. | 1000-1060 | 10.000-10.600. | 677-820 | 8.500-10.300 | ≥1990. | ≥25000. | 191-215 | 24-27 | |
XGS28M. | 1040-1100. | 10.400-11.000 | 318-804. | 4.000-10.100. | ≥398 | ≥5000. | 207-231 | 26-29 | |
XGS28 | 1040-1100. | 10.400-11.000 | 677-820 | 8.500-10.300 | ≥1194. | ≥15000 | 207-231 | 26-29 | |
XGS28H. | 1040-1100. | 10.400-11.000 | 677-820 | 8.500-10.300 | ≥1990. | ≥25000. | 207-231 | 26-29 | |
XGS30M | 1070-1120 | 10.700-11.200. | 318-796. | 4.000-10.000 | ≥398 | ≥5000. | 223-247 | 28-31. | |
XGS30. | 1070-1120 | 10.700-11.200. | 700-828 | 8.800-10.400. | ≥1194. | ≥15000 | 223-247 | 28-31. | |
XGS30H. | 1070-1120 | 10.700-11.200. | 700-828 | 8.800-10.400. | ≥1990. | ≥25000. | 223-247 | 28-31. | |
XGS32M. | 1090-1150 | 10.900-11.500. | 318-804. | 4.000-10.100. | ≥398 | ≥5000. | 231-255 | 29-32 |
Fizikal和制造ciri-ciri:
苏胡居里(°C) | 700-800. |
Suhu Operasi Makesimum(°C) | 250 UNTUK SMCO5,350 UNTUK SM2CO17 |
kerintangan(μohm.cm) | 50-90 |
Kekerasan(HV) | 450-600. |
ketumpatan(g / cm3) | 8,0-8,5. |
Relatif Recoil Kebolehtelapan(μrec) | 1.1 |
Ketepuan Field Kekuatan,Koe(ka / m) | 37.5(3000) |
Suhu Pekali Br(%/°C) | -0.05 -0.03〜 |
Suhu Pekali IHC(%/°C) | -0,25〜-0,19. |